Fine Plus>Product Information>Home |
 |
 |
| |
 |
| High strength, High transparency, Easy to print, High restiance to heat, Easy to form |
| |
 |
1.
Polycarbonate film
 Prodcucion specfication |
| |
SPEC' |
Weight |
(Pallet Packing |
Remarks
|
Thickness
(mm) |
Width
(mm) |
Length
(mm) |
Roll / Pallet |
Weight (Kg) |
ROLL |
0.100 |
930 |
600 |
66.96 |
6 |
401.76 |
6" Core
|
0.125 |
930 |
500 |
69.75 |
6 |
418.50 |
0.178 |
930 |
335 |
66.55 |
6 |
399.28 |
|
0.200 |
930 |
305 |
68.08 |
6 |
408.46 |
|
0.250 |
930 |
244 |
68.08 |
6 |
408.46 |
|
0.300 |
930 |
200 |
66.96 |
6 |
401.76 |
|
0.380 |
930 |
183 |
77.61 |
6 |
465.64 |
|
| |
0.178 |
1,220 |
280 |
72.97 |
6 |
437.79 |
|
0.200 |
1,220 |
250 |
73.20 |
6 |
439.20 |
|
0.250 |
1,220 |
200 |
73.20 |
6 |
439.20 |
|
0.300 |
1,220 |
165 |
72.47 |
6 |
434.81 |
|
0.380 |
1,220 |
130 |
72.32 |
6 |
433.93 |
|
|
|
|
|
SPEC' |
Weight |
Craft Packing |
Pallet |
Thickness
(mm) |
Width
(mm) |
Length
(mm) |
|
Weight
(Kg) |
|
Weight
(Kg) |
SHEET |
0.500 |
915 |
1,830 |
1.00 |
20 |
20.09 |
20 |
20.09 |
0.700 |
915 |
1,830 |
1.41 |
15 |
21.10 |
15 |
21.10 |
0.800 |
915 |
1,830 |
1.61 |
15 |
24.11 |
15 |
24.11 |
1.000 |
915 |
1,830 |
2.01 |
10 |
20.09 |
10 |
20.09 |
1.500 |
915 |
1,830 |
3.01 |
7 |
21.10 |
7 |
21.10 |
| |
0.500 |
1,000 |
2,000 |
1.20 |
20 |
24.00 |
20 |
24.00 |
0.700 |
1,000 |
2,000 |
1.68 |
15 |
25.20 |
15 |
25.20 |
0.800 |
1,000 |
2,000 |
1.92 |
15 |
28.80 |
15 |
28.80 |
1.000 |
1,000 |
2,000 |
2.40 |
10 |
24.00 |
10 |
24.00 |
1.200 |
1,000 |
2,000 |
2.88 |
10 |
28.80 |
10 |
28.80 |
1.500 |
1,000 |
2,000 |
3.60 |
7 |
25.20 |
7 |
25.20 |
|
|
| Physical Properties of Polycarbonate Film |
Property |
Units |
Test Method |
Result |
| General |
|
|
|
| Weight |
~ |
ASTM D792 |
1.2 |
| Water Absorption 24 hrs. |
% |
ASTM D570 |
0.12 |
| Mechanical Properties |
|
|
|
| Tensile Strength, Untimate |
psi |
ASTM D638 |
9,500 |
| Tensile Modulus |
psi |
ASTM D638 |
340,000 |
| Flexural Strength at 5% Strain |
psi |
ASTM D790 |
14,000 |
| Flexural Modulus |
psi |
ASTM D790 |
332,000 |
| Elongation |
% |
ASTM D638 |
100 |
| Izod Impact Strength, Notched |
ft-lbs/in |
ASTM D256A |
16 |
| Rockwell Hardness |
R scale |
ASTM D785 |
115 |
| Thermal Properties |
|
|
|
| Heat Deflection Temperature 264psi |
¢µ |
ASTM D648 |
270 |
| Heat Deflection Temperature 66psi |
¢µ |
ASTM D648 |
280 |
| Coefficient of Thermal Conductivity |
in/in/¢µ |
ASTM D696 |
3.75x10e -5 |
| Brittle Temperature |
¢µ |
ASTM D746 |
-200 |
| Optical Properties |
|
|
|
| Transmitance |
% |
ASTM D1003 |
>86 |
| Haze |
% |
ASTM D1003 |
<1 |
| Electrical Properties |
|
|
|
| Dielectric Constant 10Hz |
- |
ASTM D150 |
2.36 |
| Dielectric Constant 60Hz |
- |
ASTM D150 |
3.17 |
| Volume Resistivity |
ohm-§¯ |
ASTM D257 |
8.20E+16 |
| Arc Resistance |
|
|
|
| Stainless Steel Strip Electrodes |
sec |
ASTM D495 |
10 |
| Tungsten Electrode |
sec |
ASTM D495 |
120 |
|
|
| 2. Acrylic Film |
| Physical Properties of Acrylic Film |
division |
Test item |
Test Method |
Units |
PropertyProperties |
before coating |
After
coating |
Property Properties |
Weight |
ASTM D 792 |
g/§² |
1.19 |
1.19 |
| Electric line clarity |
ASTM D 1003 |
% |
92 |
93 |
| Haze |
ASTM D 1003 |
% |
1.0 |
1.0 |
| Refractive Index |
ASTM D 1003 |
- |
1.5 |
1.52 |
| Yellowing |
ASTM D 638 |
YI |
1.5 or less |
1.5 or less |
Mechanical Properties |
Tensile Strength |
ASTM D 638 |
Mpa |
75 |
64 |
| Refractive Elasticity |
ASTM D 790 |
Mpa |
98 |
294 |
| Bending Strength |
ASTM D 790 |
Mpa |
118 |
90 |
| Dyratat impact strength |
DIN 53453 |
Kg-§¯/§¯ |
5.1 |
4 |
Surface friction |
Hardness |
ASTM D 785 |
M-scale |
100 |
100 |
| Wear resistance |
ASTM D 1004 |
%(haze) |
15 |
3 |
| Steel wool test(note.1) |
ASTM D |
g |
1000 |
10 |
| Pencil hardness |
JIS D 1004 |
H |
2 |
6-7 |
Endurance |
Heat resistance |
24 hrs at 70¡É |
- |
No change |
No change |
| Warm water resistance |
24 hrs in a warm bath
at 40¡É |
- |
No change |
No change |
| THERMALCYCLE TEST |
10 hrs at -30¡É |
- |
No change |
No change |
| 10 hrs at 25¡É |
- |
No change |
No change |
Thermal Properties |
Weight transformation
temperature |
8.5§¸/§² |
ASTM D |
¡É |
95 |
95 |
| 4.6§¸/§² |
104 |
104 |
| Coefficient of linear (thermal) expansion |
ASTM E 228 |
§¯/§¯/¡É |
0.6x10E-5 |
0.6x10E-5 |
Electrical Properties |
Surface resistance |
ASTM D |
§Ù |
10E16 |
10E16 |
| Dielectric breakdown strength |
ASTM D |
kV/mm |
20 |
20 |
Drug resistance |
Hydrochloric acid(5%) |
- |
- |
No change |
No change |
| Alkali(5%) |
- |
- |
No change |
No change |
| Saline solution(10%) |
- |
- |
No change |
No change |
| Methanol |
- |
- |
No change |
No change |
| Ethanol |
- |
- |
No change |
No change |
| Toluene |
- |
- |
No change |
No change |
| Gasoline |
- |
- |
No change |
No change |
|
| note1 ¢º Lowest weight is indicated when a blur clearly appers from a sample after pushing wool#1000 steel wall of a round pad (area:4.81§²)and
turning it at 40rpm 100 times. |
|
 |
1. Polycarbonate film
Electronic product decoration(laundry machine, TV, refrigerator), gauge board and toy cover(forming)
Electronic air product(partition), plate print, electronic part and front panel
2. Acryl film
Each type of advertisement signboard, illumination device, vacuum forming, household electric appliance, interior decoration, nameplate of audio device and industrial case |
| |
 |
| Contact the main factory or the sales department, or send an e-mail |
| |
|
|
|