Type | SPEC | Weight | Pallet Packing | Remarks | |||
---|---|---|---|---|---|---|---|
Thickness | Width | Length | Roll/Pallet | Weight | |||
ROLL | 0.100 | 930 | 600 | 66.96 | 6 | 401.76 | 6"Core |
0.125 | 930 | 500 | 69.75 | 6 | 418.50 | ||
0.178 | 930 | 335 | 66.55 | 6 | 399.28 | ||
0.200 | 930 | 305 | 68.08 | 6 | 408.46 | ||
0.250 | 930 | 244 | 68.08 | 6 | 408.46 | ||
0.300 | 930 | 200 | 66.96 | 6 | 401.76 | ||
0.380 | 930 | 183 | 77.61 | 6 | 465.64 | ||
0.178 | 1,220 | 280 | 72.97 | 6 | 437.79 | ||
0.200 | 1,220 | 250 | 73.20 | 6 | 439.20 | ||
0.250 | 1,220 | 200 | 73.20 | 6 | 439.20 | ||
0.300 | 1,220 | 165 | 72.47 | 6 | 434.81 | ||
0.380 | 1,220 | 130 | 72.32 | 6 | 433.93 |
Type | SPEC | Weight | Craft Packing | Pallet Packing | ||||
---|---|---|---|---|---|---|---|---|
Thickness | Width | Length | Q’ty | Weight | Q’ty | Weight | ||
SHEET | 0.500 | 915 | 1,830 | 1.00 | 20 | 20.09 | 20 | 20.09 |
0.700 | 915 | 1,830 | 1.41 | 15 | 21.10 | 15 | 21.10 | |
0.800 | 915 | 1,830 | 1.61 | 15 | 24.11 | 15 | 24.11 | |
1.000 | 915 | 1,830 | 2.01 | 10 | 20.09 | 10 | 20.09 | |
1.500 | 915 | 1,830 | 3.01 | 7 | 21.10 | 7 | 21.10 | |
0.500 | 1,000 | 2,000 | 1.20 | 20 | 24.00 | 20 | 24.00 | |
0.700 | 1,000 | 2,000 | 1.68 | 15 | 25.20 | 15 | 25.20 | |
0.800 | 1,000 | 2,000 | 1.92 | 15 | 28.80 | 15 | 28.80 | |
1.000 | 1,000 | 2,000 | 2.40 | 10 | 24.00 | 10 | 24.00 | |
1.200 | 1,000 | 2,000 | 2.88 | 10 | 28.80 | 10 | 28.80 | |
1.500 | 1,000 | 2,000 | 3.60 | 7 | 25.20 | 7 | 25.20 |
Technical Data | Test Method | Unit | Value | Unit | Value | ||
---|---|---|---|---|---|---|---|
Physical Properties | Specific Gravity | ASTM D792 | - | 1.20 | - | 1.20 | |
Water Absorption, 23℃, 24 hr | ASTM D570 | % | 0.12 | % | 0.12 | ||
Optical Properties | Transmittance | ASTM D1003 | % | 86 | % | 86 | |
Haze | ASTM D1003 | % | 1.0 | % | 1.0 | ||
Mechanical Properties | Tensile Strength | ASTM D638 | psi | 9500 | Mpa | 65.5 | |
Tensile Modules | ASTM D638 | psi | 340000 | Mpa | 2344.2 | ||
Refractive Elasticity @5% pressure | ASTM D790 | psi | 14000 | Mpa | 96.5 | ||
Bending Strength | ASTM D790 | psi | 332000 | Mpa | 2289.0 | ||
Elongation | ASTM D638 | % | 100 | % | 100 | ||
Rockwell Hardness | ASTM D785 | R Scale | 115 | R Scale | 115 | ||
Thermal Properties | Load-deformation Temperature | (@ 1.820 Mpa) | ASTM D648 | ℉ | 270 | ℃ | 132 |
(@ 0.455 Mpa) | 280 | 137 | |||||
Heat Conductivity | ASTM D696 | in/in/℉ | 3.75×10-5 | ㎝/㎝/℃ | 6×10e-5 | ||
Sensitive Temperature | ASTM D746 | ℉ | -200 | ℃ | -128 | ||
Ignition | Dielectric Constant @10Hz | ASTM D150 | - | 2.36 | - | 2.36 | |
Dielectric Constant @60Hz | ASTM D150 | - | 3.17 | - | 3.17 | ||
Volume Resistivity | ASTM D257 | ohm-cm | 8.20E+16 | ohm-cm | 8.20E+16 | ||
Stainless Steel Strip Electrodes | ASTM D495 | sec | 10 | sec | 10 | ||
Tungsten Electrode | ASTM D495 | sec | 120 | sec | 120 |
※ The above in formation is typical values only, not for warranty purpose.